Design and mechanical tests of basalt fiber cloth with MAH grafted reinforced bamboo and poplar veneer composite

Liu, Hongguang; Luo, Bin; Shen, Shijie; Li, Li

doi:10.1007/s00107-018-1378-9

Original
Published: 07 December 2018

Design and mechanical tests of basalt fiber cloth with MAH grafted reinforced bamboo and poplar veneer composite

Hongguang Liu¹,
Bin Luo¹,
Shijie Shen¹ &
Li Li¹

European Journal of Wood and Wood Products volume 77, pages 271–278 (2019)Cite this article

238 Accesses
1 Citations
Metrics details

Abstract

High performance fibers are widely applied to wood-based composites as reinforcement to improve mechanical performance of composites. Design and mechanical performance tests of basalt fiber cloth reinforced bamboo and poplar veneer (BFRBV) composite are presented in this paper. The fiber surface usually needs to be treated to increase the bonding strength of composites. The optimization scheme of maleic anhydride (MAH) treatment parameters was obtained by orthogonal experiment, namely temperature of 50 °C, time of 3 h and concentration of 0.08 mol/L. The mechanical performance of wood composites treated with three methods of fiber surface treatment, namely no treatment, KH550 treatment and KH550 and MAH co-treatment, was tested. The results indicated that the mechanical performance indexes of BFRBV composite were greatly improved with KH550 and MAH co-treatment. In comparison with no treatment, dry shear strength was improved by 113.3%, wet shear strength by 126.2%, peel rate was reduced from 20.15% to 0, and MOR was improved by 35.4%.

This is a preview of subscription content, access via your institution.

Access options

Buy single article

Instant access to the full article PDF.

34,95 €

Price includes VAT (Hong Kong/P.R.China)
Tax calculation will be finalised during checkout.

') var head = document.getElementsByTagName("head")[0] var script = document.createElement("script") script.type = "text/javascript" script.src = "https://buy.springer.com/assets/js/buybox-bundle-52d08dec1e.js" script.id = "ecommerce-scripts-" + timestamp head.appendChild(script) var buybox = document.querySelector("[data-id=id_"+ timestamp +"]").parentNode ;[].slice.call(buybox.querySelectorAll(".buying-option")).forEach(init) function init(buyingOption, index) { var form = buyingOption.querySelector("form") if (form) { var formAction = form.getAttribute("action") document.querySelector("#ecommerce-scripts-" + timestamp).addEventListener("load", bindModal(form, formAction, timestamp, index), false) } } function bindModal(form, formAction, timestamp, index) { var weHasBrowserSupport = window.fetch && Array.from return function() { console.log("ecommerce-scripts loaded, attempting to init modal …") var Buybox = EcommScripts ? EcommScripts.Buybox : null var Modal = EcommScripts ? EcommScripts.Modal : null if (weHasBrowserSupport && Buybox && Modal) { var modalID = "ecomm-modal_" + timestamp + "_" + index var modal = new Modal(modalID) modal.domEl.addEventListener("close", close) function close() { form.querySelector("button[type=submit]").focus() } var cartURL = "/cart" var cartModalURL = "/cart?messageOnly=1" form.setAttribute( "action", formAction.replace(cartURL, cartModalURL) ) var formSubmit = Buybox.interceptFormSubmit( Buybox.fetchFormAction(window.fetch), Buybox.triggerModalAfterAddToCartSuccess(modal), function() { form.removeEventListener("submit", formSubmit, false) form.setAttribute( "action", formAction.replace(cartModalURL, cartURL) ) form.submit() } ) form.addEventListener("submit", formSubmit, false) document.body.appendChild(modal.domEl) } else { console.log("binding failed:", weHasBrowserSupport, EcommScripts) } } } })()

Fig. 1

Fig. 2

Fig. 3

Fig. 4

Fig. 5

Fig. 6

References

Al-Malaika S (1997) Reactive Modifiers for Polymers. Blackie Academic & Professional, London

Book Google Scholar
Bal BC, Bektaş İ, Mengeloğlu F, Karakuş K, Demir H (2015) Some technological properties of poplar plywood panels reinforced with glass fiber fabric. Constr Build Mater 101:952–957

Article Google Scholar
Busfield WK, Brandup J, Immergut EH (1989) Polymer Handbook, 3rd edn. Wiley, New York

Google Scholar
Chen J, Wang Y, Gu C, Liu J, Liu Y, Li M, Lu Y (2013) Enhancement of the mechanical properties of basalt fiber-wood-plastic composites via maleic anhydride grafted high-density polyethylene (MAPE) addition. Materials 6:2483–2496

Article CAS PubMed PubMed Central Google Scholar
Dhand V, Mittal G, Rhee KY, Park S-J, Hui D (2015) A short review on basalt fiber reinforced polymer composites. Compos B 73:166–180

Article CAS Google Scholar
Fiore V, Scalici T, Bella DG, Valenza A (2015) A review on basalt fibre and its composites. Compos B 74:74–94

Article CAS Google Scholar
GB/T 17657 (2013) Test methods of evaluating the properties of wood-based panels and surface decorated wood-based panels. Standardization Administration of China, Beijing

Google Scholar
Greco A, Maffezzoli A, Casciaro G, Caretto FC (2014) Mechanical properties of basalt fibers and their adhesion to polypropylene matrices. Compos B 67:233–238

Article CAS Google Scholar
Iorio M, Santarelli ML, González-Gaitano G, González-Benito J (2018) Surface modification and characterization of basalt fibers as potential reinforcement of concretes. Applied Surface Science (427):1248–1256
Jie D, Weitao X, Shuangbao Z, Shijie S (2007) Application and fiber-reinforced polymer in engineered wood composites field. China Wood Based Panels (1): 17–20
Jinfen L, Fenghe M, Zhu L (2013) Effect of Maleic anhydride graft on properties of PP/ABS composite. China Plast Ind 41(6):60–63

Google Scholar
Junshi Z, Zhengdong Z, Jinlin W (2012) Research progress of glulam and glass fiber reinforced polymer composites. J West China For Sci 41(2):106–109

Google Scholar
Lifeng Z, Baohua G, Zengmin Z (2001) Synthesis of PP-g-MAH via solid grafting with a quantitative express method for analyzing MAH content. J Tsinghua Univ (Sci Technol) 41(10):5–8

Google Scholar
Liu T, Yu F, Yu X, Zhao X, Lu A, Wang J (2012) Basalt fiber reinforced and elastomer toughened polylactide composites: Mechanical properties, rheology, crystallization, and morphology. J Appl polym Sci 125:1292–1301

Article CAS Google Scholar
Manikandan V, Winowlin Jappes JT, Suresh Kumar SM, Amuthakkannan P (2012) Investigation of the effect of surface modifications on the mechanical properties of basalt fibre reinforced polymer composites. Compos B 43:812–818

Article CAS Google Scholar
Moad G (1999) The synthesis of polyolefin graft copolymers by reactive extrusion. Prog Polym Sci (24):81–142
Moad G, Solomon DH (1995) The Chemistry of Free Radical Polymerization. Pergamon, Oxford

Google Scholar
Pak S, Park S, Song YS, Lee DL (2018) Micromechanical and dynamic mechanical analyses for characterizing improved interfacial strength of maleic anhydride compatibilized basalt fiber/polypropylene composites. Compos Struct (193):73–79
Russell KE, Kelusky EC (1988) Grafting of maleic anhydride to n-eicosane. J Polym Sci Part A Polym Chem 26:2273–2280

Article CAS Google Scholar
Sipos A, McCarthy J, Russell KE (1989) Kinetic studies of grafting of maleic anhydride to hydrocarbon substrates. J Polym Sci Part A Polym Chem 27:3353–3362

Article CAS Google Scholar
Sliseris J, Frolovs G, Rocens K, Goremikins V (2013) Optimal design of GFRP-plywood variable stiffness plate. Procedia Eng 57:1060–1069

Article CAS Google Scholar
Song Q-X, Liu H-W, Zhong Z-L, Xu P (2010) Effect of silane coupling agent treatment on tensile properties of single basalt filament. J Tianjin Polytech Univ 29(1):19–22

CAS Google Scholar
Tiwaria S, Bijweb J (2014) Surface treatment of carbon fibers - a review. Procedia Technol 14:505–512

Article Google Scholar
Wei P, Wang BJ, Zhou D, Dai C, Wang Q, Huang S (2013) Mechanical properties of poplar laminated veneer lumber modified by carbon fiber reinforced polymer. BioResources 8(4):4883–4898

Article Google Scholar
Zhang X, Zhu Y, Jiang S, Zhang Q (2011) Mechanical and aging resistance properties of bamboo-wood composite LVL. China For Sci Technol 25(5):55–57

CAS Google Scholar

Download references

Acknowledgements

The authors are grateful for the support of the Fundamental Research Funds for the Central Universities (NO: 2017JC11), China Scholarship Council (NO: 201706515040), MOE Key Laboratory of Wooden Material Science and Application, Beijing Key Laboratory of Wood Science and Engineering.

Author information

Authors and Affiliations

College of Material Science and Technology, Beijing Forestry University, Beijing, 100083, China

Hongguang Liu, Bin Luo, Shijie Shen & Li Li

Authors

Hongguang Liu

View author publications

You can also search for this author in PubMed Google Scholar
Bin Luo

View author publications

You can also search for this author in PubMed Google Scholar
Shijie Shen

View author publications

You can also search for this author in PubMed Google Scholar
Li Li

View author publications

You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Li Li.

Additional information

Publisher’s Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Liu, H., Luo, B., Shen, S. et al. Design and mechanical tests of basalt fiber cloth with MAH grafted reinforced bamboo and poplar veneer composite. Eur. J. Wood Prod. 77, 271–278 (2019). https://doi.org/10.1007/s00107-018-1378-9

Download citation

Received: 17 February 2017
Published: 07 December 2018
Issue Date: 04 March 2019
DOI: https://doi.org/10.1007/s00107-018-1378-9

Buy single article

Cite this article

Share this article